Spray Polyurea Overweight Anti-corrosion Coating

Page view:
Name

Spray Polyurea Overweight Anti-corrosion Coating

没有此类产品
Details

Name      Spray Polyurea Overweight Anti-corrosion Coating
Model     HTSPUA-4001
Description  The coating system consists of amine-terminated resin, arylamine chain extender and MDI prepolymer. The product is dual-component, self-cured and thick coating anti-corrosion material.
Applications   Used in industries of oil, petrifaction and chemicals and used for anticorrosion of iron, such as oil tanks, saline tanks, electrolytic bathes, ship and warship decks and naval vessel grounds, offshore facilities, steel piles and bay bridges.

Coating Property

Solid Content

100%

Velocity (25℃)

≤1000mPa.s

Density (25℃)

A: 1.080-1.160 g/cm3 
R: 1.030-1.100 g/cm3

Theoretical Coating Amount (Dry Film: 1mm Thickness)

1.1kg/m2

Volume Mixing Ratio

A:R = 1:1

Shelf Life

1 year

Curing Characteristics

Gelation Time

15 seconds

Touch Drying Time

80 seconds

Curing Time

24 hours

Maximum Strength

7 days

Coating Property*

Tensile Strength

25MPa

Hardness

60D

Tearing Strength

60KN/m

Elongation

40%

Medium Resistance Performance

Good

* It needs seven days for the polyurea coating to be completely aggregated and reach final strength. 
 Coating equipment status determines the property of coating.
 A test sample is cured in a thermostat of 65-70℃ for 24 hours

 